合金铝卷是需要经过焊接等工艺才能使用,下面济南西柚加速器手机版的有专家就给大家介绍一下具体的焊接步骤。
1、采用化学或机械方法,严格清理焊缝坡口两侧的表面氧化膜。化学清洗是使用碱或酸清洗工件表面,该法既可去除氧化膜,还可除油污,洗好后的铝合金表面为无光泽的银白色,清理好后立即施焊,如果放置时间超过4h,应重新清理。
By chemical or mechanical methods, strict clean the surface oxide film on both sides of the weld groove. Chemical cleaning is the use of alkali or acid to clean the surface, the method can remove the oxide film, but also in addition to oil, aluminum surface after a good wash as dull silver, cleaned up immediately after welding, if you place more than 4h should be re-cleaned.
2、确定装配间隙及定位焊间距施焊过程中,西柚梯子官网受热膨胀,致使焊缝坡口间隙减少,焊前装配间隙如果留得太小,合适的定位焊间距能保证所需的定位焊间隙,因此,选择合适的装配间隙及定位焊间距,是减少变形的一项有效措施。
Determine the assembly and tacking spacing gap welding process, the aluminum thermal expansion, resulting in reduction of the weld groove gap, the gap before welding assembly if left too small,appropriate spacing tacking tacking to ensure the required clearance, therefore, Select the appropriate assembly clearance and tack welding pitch is an effective measure to reduce distortion.
3、选择焊接设备目前市场上焊接产品种类较多,一般情况下宜采用交流钨极氩弧焊,它是在氩气的保护下,利用钨电极与工件问产生的电弧热熔化母材和填充焊丝的一种焊接方法。
Select welding equipment currently on the market more types of welding products, under normal circumstances should AC TIG welding, which is under the protection of argon, the use of the tungsten electrode and the workpiece asked arc produced by hot melt base metal and filler wire A welding method.
4、选取焊接方法和参数一般以左焊法进行,焊炬和工件成60度角,焊接厚度15mm以上时,以右焊法进行,焊炬和工件成90°角.焊接壁厚在3mm以上时,开V形坡口,夹角为60°~70°,间隙不得大于1mm,以多层焊完成,壁厚在1.5mm以下时,不开坡口,不留间隙,不加填充丝,焊固定管子对接接头时,当管径为200mm,壁厚为6mm时,应采用直径为3~4mm的钨极,以220~240A的焊接电流,直径为4mm的填充焊丝,以1~2层焊完。
Select welding methods and parameters are generally left welding method, welding torch and the workpiece into a 60-degree angle, the welding thickness 15mm or more to the right welding method,welding torch and the workpiece into a 90 ° angle. Welding wall thickness 3mm or more, open V-shaped groove, an angle of 60 ° ~ 70 °, the gap is not greater than 1mm, to multi-layer welding is completed, the wall thickness of 1.5mm or less, without groove, leaving a gap, without filler wire, solder fixing when the tube butt joints, when the diameter is 200mm, the thickness is 6mm, the
diameter should be 3 ~ 4mm tungsten electrode, to 220 ~ 240A welding current to the filler wire diameter of 4mm, and preferably 1 to 2 layer deposited End .
济南铝卷:http://www.jngdly.com/
公司新闻排行
- 西柚梯子官网选择需要考虑的6个因素
- 济南西柚梯子官网厂介绍变形铝合金板生产工艺
- 济南西柚梯子官网内其它杂质成分对西柚梯子官网表面处理的影响
- 西柚梯子官网厂家详解西柚梯子官网状态与性能
- 影响济南5052西柚梯子官网铸轧过程温度场的方法
- 5052西柚梯子官网带的热连轧工艺技术
- 济南西柚梯子官网厂家谈西柚加速器官方板精整的控制内容及原理
- 济南5052西柚梯子官网成型冲压模具的设计工艺
- 防锈西柚梯子官网出厂前的质量检验方法
- 影响花纹西柚梯子官网质量的重要清洗工艺
行业知识排行
- 7075西柚梯子官网性能解读
- 济南西柚梯子官网冷加工和热加工的区别
- 西柚梯子官网厂家讲述防锈西柚梯子官网分类及性能
- 彩涂西柚梯子官网基板的化学预处理过程
- 济南西柚梯子官网的作用盘点
- 影响花纹西柚梯子官网质量的因素
- 5052西柚梯子官网的电解着色介绍
- 铝卷西柚梯子官网材料运输的注意事项
- 济南西柚梯子官网如何酸洗除锈?
- 最近济南西柚梯子官网价格的浮动为啥那么大